Material im weichgeglühtem Zustand vorliegen
DIN | Alloy | UNS | AISI | AFNOR | B.S. | Registered work's label |
---|---|---|---|---|---|---|
2.4066 | alloy 200 | N 02200 | NA 12 | Nickel 200 | ||
2.4360 | alloy 400 | N 04400 | Nu 30 | Na13 | Monel® 400 Nicorros®alloy 400 | |
2.4858 | alloy 825 | N 08825 | NC 21 FeDu | NA 16 | Incoloy® 825 |
- pre-heat to 392°F if material width >0.4"
- when using covered rod electrodes, mind the low C and Si content
- Beim Schweißen unter Gas kein wasserstoff-oder stickstoffhaltiges Gas verwenden
- ???
- preheating not required
- avoid gas welding
- gezielte Wärmeführung
- generally no heat treatment necessary after welding process
- special post heat treating not required
- use material in soft-annealed state
- material is heat-sensitive , requires low heat input
- material has to be normalized or tempered
- normal weldability
- Vorwärm- und Arbeitstemperatur max.200°C
- pre-heat 302°F
- pre-heat 212°F (>10mm)
- pre-heat 662°F
- no heat treatment necessary before or after welding process
- material is weldable in all widths using aforementioned techniques
- interpass temperature must not go over 302°F
- Zwischenlagetemperatur max 120°C
Liability exclusion
All aforementioned specifications serve as a general orientation and have to be reviewed depending on the conditions of use.(c) 2012 M. Woite GmbH, Postbox, D-40671 Erkrath | Phone +49 (211) 24 40 91 - Fax +49 (211) 24 92 28 | www.m-woite.com - woite@woite-edelstahl.com