Material No.: alloy 200
Description
|
| ||||||||||||||||||||||
|
Chemical Composition
C | Mn | S | Si | Ni | Cu | Fe | Fe | Mg | Ti | ||
---|---|---|---|---|---|---|---|---|---|---|---|
alloy 200 | Min % | 99,00 | |||||||||
Max % | 0,15 | 0,35 | 0,010 | 0,35 | 0,25 | 0,40 | |||||
ASTM B 161 | |||||||||||
2.4066 | Min % | 99,20 | |||||||||
Max % | 0,10 | 0,35 | 0,005 | 0,25 | 0,40 | 0,15 | 0,10 | ||||
(Key to Steel 2010) | |||||||||||
N 02200 | Min % | 99,00 | |||||||||
Max % | 0,15 | 0,35 | 0,010 | 0,35 | 0,25 | 0,40 | |||||
ASTM B 161 |
Physical properties
Property | Value |
---|---|
Density: kg/dm3 | 8,89 |
Hardness: HBW / HV | <=130 / 110 |
Permeabilität bei 20°C | ferromagnetic |
magnetic properties | good |
Temperature T °C/F (°C/F) | Specific heat J / kgK (Btu / lb °F) | Thermal conductivity W/mK (Btu·in / ft2·h·°F) | Electric resistance µΩ · cm (Ω circ mill / ft) | Modulus of elasticity kN/mm2 (103 ksi) | Expansion rate from 70°F bis T 10-6 / K (10-6 / °F) |
---|---|---|---|---|---|
20 | 456 | 79 | 8,5 | 207 | 10,1 (5,8) |
100 | 355 (0,091) | 75 (505) | 4,5 (33) | 218 - | 13,3 |
300 | 426 (0,102) | 71,5 (500) | 8,5 (51) | 207 (30) | 14,3 |
500 | 456 (0,109) | 70,5 (490) | 9 (54) | 205 (29,7) | 15,2 |
100/212 (100/212) | 475 (-) | 66,5 (-) | 13 - | 200 - | 13,3 - |
300/572 (316/600) | 570 (0,139) | 57 (390) | 26 (162) | 190 (27,3) | 14,3 (8,0) |
500/932 (538/1000) | 525 (0,128) | 57,5 (405) | 37 (239) | 175 (24,7) | 15,2 (8,5) |
800/1472 (871/1600) | 565 (0,137) | 64 (455) | 45 (285) | 140 (19,6) | 16,2 (9,1) |
1000/1832 (982/1800) | 590 (0,144) | 69 (470) | 51 (305) | -- -- | 16 ,(9,3) |
Mechanical properties (20°C / 68°F)
Yield strenght (20°C/68°F) Rp0,2 - N/mm2 /ksi | 207 / 30 | ||
---|---|---|---|
Tensile strength(20°C/68°F)-ksi | 65 | ||
Elongation (A5)% | 45 | ||
impact energy ISO-V | |||
Remarks |
Temparature information
Application area | ||
---|---|---|
Operation temperature | -459 ºF to 572 ºF | |
Explanation report | over 572°F prefereably low-coaled version (2.4068) |
Solution heat treatment | ||
---|---|---|
Working temperature | 1292 ºF to 1562 ºF |
low-strain annealing | ||
---|---|---|
Working temperature | 1292 ºF to 1562 ºF |
Solution heat treatment | ||
---|---|---|
Working temperature | 2192 ºF to 1472 ºF | |
Explanation report | air cooling |
Standards / information
Standards | Desciption |
---|---|
ASTM B 160 | Standard Specification for Nickel Rods and Bars |
ASTM B 161 | Standard Specification for Nickel Seamless Pipes and Tubes |
ASTM B 162 | Standard Specifications for nickel sheet metal and ribbons |
ASTM B 163 | Standard Specifications for seamless nickel and nickel alloy condensers and heat-exchanger tubes |
ASTM B 366 | Standard Specification for Factory-Made Wrought nickel and nickel alloy fittings |
ASTM B 564-06 | Standard Specification for Nickel Alloy Forging |
ASTM B 725 | Standard Specification for Welded Nickel and Nickel Cooper Alloy Pipe |
DIN 17740 (09/2002) | nickel in wrought material |
DIN 17751 (2002/09) | tubes out of nickel with nickel-wrought alloy properties |
Process information
Cold forming | in annealed state, great modifications require intermittent annealing |
---|
Chip removing process | preferably in annealed state - slow cutting rate due to tendency to cold-work hardening |
---|
Welding | |
---|---|
- Material classification acc. CEN ISO/TR 15608 | 41 |
- Type | well weldable |
- Add. material | 2.4156; 2.4155 |
- Hints | No translation! when using covered rod electrodes, mind the low C and Si content |
Main fields of application
Details of application | production of caustic soda, chlorine, hydrogen chloride, food processing, production of soaps and cleaning agents |
---|---|
Certifications | |
Anlagen zur Salzherstellung | zur Herstellung von Chlor,Chlorwasserstoff zur Eindampfung von Ätznatron zur Fluorerzeugung Waschmittel- und Seifenherstellung |
Anlagen für Kunststoffherstellung | zur Salzherstellung |
Eindampfung von Ätznatron | |
Chemical Industry | Fluor, Chlorwasserstoff |
petrochemical industry |
Range of products
Product type | Product |
---|---|
Plates / Sheets | plates/sheets plate/sheet cuts |
Rotating components | fittings from barsteel |
Fittings | welded elbows welded reductions Welded T-pieces seamless elbows seamless reductions seamless T-pieces |
Flanges / Collars / Flared tube ends | flared tube end collars various flanges (weld neck flange,blind flange etc.) |
Pipes / Tubes | welded pipes/tubes welded square pipes/tubes seamless pipes/tubes |
Bar steel | flat steel section steel round bar steel hexagon steel |
Liability exclusion
All aforementioned specifications serve as a general orientation and have to be reviewed depending on the conditions of use.(c) 2012 M. Woite GmbH, Postbox, D-40671 Erkrath | Phone +49 (211) 24 40 91 - Fax +49 (211) 24 92 28 | www.m-woite.com - woite@woite-edelstahl.com