Material No.: AISI 310 S
Description
|
|
Chemical Composition
C | Mn | P | S | Si | Cr | Ni | Mo | N | ||
---|---|---|---|---|---|---|---|---|---|---|
AISI 310 S | Min % | 24,00 | 19,00 | |||||||
Max % | 0,08 | 2,00 | 0,045 | 0,030 | 1,00 | 26,00 | 22,00 | 0,75 | ||
AISI 310 S | ||||||||||
1.4845 S 31008 | Min % | 24,00 | 19,00 | |||||||
Max % | 0,08 | 2,00 | 0,045 | 0,030 | 1,00 | 26,00 | 22,00 | 0,75 | ||
UNS :S 31008 (ASTM A 312-TP 310 S) |
Physical properties
Property | Value |
---|---|
Density: kg/dm3 | 7,9 |
Hardness: HB 30 | <= 192 |
magnetizable | no |
Temperature T °C/F (°C/F) | Specific heat J / kgK (Btu / lb °F) | Thermal conductivity W/mK (Btu·in / ft2·h·°F) | Electric resistance µΩ · cm (Ω circ mill / ft) | Modulus of elasticity kN/mm2 (103 ksi) | Expansion rate from 70°F bis T 10-6 / K (10-6 / °F) |
---|---|---|---|---|---|
20 / 68 | 500 (--) | 15 (--) | 0,93 (--) | 195 (--) | 16,5 (--) |
100 /212 | 0,93 (--) | 195 (--) | 16,5 (--) | ||
200 / 392 | 1,03 (--) | 182 (--) | 17,0 (--) | ||
400 /752 | 1,22 | 170 (--) | 18,0 (--) | ||
500 / 932 | 19 (--) | ||||
600 /1112 | 1,37 (--) | 155 (--) | 18,5 (--) | ||
1000 / 1832 | 1,45 (--) | 120 (--) | 19,5 (--) |
Temp. | Creep strain limit | Creep strain limit | Creep rupture strength | Creep rupture strength | Creep rupture strength |
---|---|---|---|---|---|
°C/°F | 1% (10 000h) | 10 000 h | 100 00 h | °C/°F | N/mm2 /ksi | N/mm2 /ksi | N/mm2 /ksi |
500 / 932 | |||||
600 / 1112 | 90 /13,0 | 130 / 18,8 | 80 / 11,6 | ||
700 / 1292 | 30 / 4,3 | 40 / 5,8 | 18 / 2,7 | ||
800 / 1472 | 10 / 1,45 | 18 / 2,6 | 7 / 1,0 | ||
900 / 1652 | 4 7 0,6 | 8,5 / 1,2 | 3 / 0,4 |
Mechanical properties (20°C / 68°F)
tensile elastic limit Re (Mpa) | >=210 | ||
---|---|---|---|
Tensile strenght Rm (Mpa) | 500-700 | ||
Elongation A5 (%) | >=35 |
Temparature information
Application area | ||
---|---|---|
Operation temperature | ºF to 1922 ºF | |
Explanation report | scaling resistance (air) up to 1922°F |
Solution heat treatment | ||
---|---|---|
Working temperature | 1922 ºF to 2012 ºF |
Solution heat treatment | ||
---|---|---|
Working temperature | 2102 ºF to 1472 ºF | |
Explanation report | fast cooldown :air |
Standards / information
Standards | Desciption |
---|
Process information
Chip removing process | requires slow cutting speed due to cold work hardening don't break contact with cutting tool |
---|
Welding | |
---|---|
- Type | well weldable WIG MAG solid wire manual arc welding (E) |
- Add. material | 1.4842 |
- Hints | no heat treatment necessary before or after welding process |
Main fields of application
Details of application | thermotechnical facilities with increased scaling resistance (up to 1922°F) |
---|---|
Certifications | |
industral furnace engineering | Ofenteile Glührohre Muffelrohre |
Power plants | |
petrochemical industry | |
crude oil |
Range of products
Product type | Product |
---|---|
Plates / Sheets | plates/sheets plate/sheet cuts |
Fittings | welded elbows welded reductions Welded T-pieces seamless elbows seamless reductions seamless T-pieces |
Flanges / Collars / Flared tube ends | various flanges (weld neck flange,blind flange etc.) |
Round bar | peeled |
Bar steel | flat steel round bar steel |