Material No.: 2.4816
Description
|
| ||||||||||||||||||||||||
|
Chemical Composition
C | Si | Mn | P | S | Cr | Ni | Cu | Co | Fe | Ti | B | Al | ||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
2.4816 | Min % | 0,05 | 14,00 | 72,00 | 6,00 | |||||||||
Max % | 0,10 | 0,50 | 1,00 | 0,020 | 0,015 | 17,00 | 0,50 | 1,50 | 10,00 | 0,30 | 0,006 | 0,30 | ||
(Key to Steel 2010) | ||||||||||||||
alloy 600 N 06600 | Min % | 14,00 | 72,00 | 6,00 | ||||||||||
Max % | 0,15 | 0,50 | 1,00 | 0,015 | 17,00 | 0,50 | 10,00 | |||||||
ASTM B 517 |
Physical properties
Property | Value |
---|---|
Density: lb/in3 | 0,306 |
Hardness: alloy 600 (HB) alloy 600H (HB) | <=195 <=185 |
Permeability at 20°C/68°F | 1,05 |
Elongation A5 (%) alloy 600 alloy 600H | 30 35 |
Temperature T °C/F (°C/F) | Specific heat J / kgK (Btu / lb °F) | Thermal conductivity W/mK (Btu·in / ft2·h·°F) | Electric resistance µΩ · cm (Ω circ mill / ft) | Modulus of elasticity kN/mm2 (103 ksi) | Expansion rate from 70°F bis T 10-6 / K (10-6 / °F) |
---|---|---|---|---|---|
20/68 | 455(0,108) | 14,8 (103 | 103 (620) | 214 (31,0) | |
100/212 | 475 | 15,8 | 104 | 209 | 13,7 |
200/392 (2047400) | 495 (0,118) | 17,0 (118) | 106 (638) | 205 (29,7) | 14,1 (7,8) |
400/752 (427/800) | 525 (0,126) | 20,0 (143) | 108 (655) | 194 (27,8) | 14,8 (8,3) |
600/1112 (649 /1200) | 572 (0,140) | 24,0 (172) | 112 (674) | 180 (25,5) | 15,4 (8,6) |
700/1292 (760/1400) | 602 (0,146) | 25,7 (186) | 112 (674) | 172 (24,2) | 15,8 (8,7) |
800/1472 (871/1600) | 620 (0,150) | 27,5 (201) | 112 (678) | 163 (22,8) | 16,1 (9,0) |
900/1652) (982/1800) | 630 (0,151) | 29,4 (215) | 113 (683) | 153 (21,0) | 16,4 (9,3) |
1000 | 635 | 31,2 | 114 | 143 | 16,9 |
Mechanical properties (20°C / 68°F)
°F | 68°F | 600°F | 900°F |
---|---|---|---|
Yield strength Rp 0.2 alloy 600 - annealed (ksi) alloy 600H - solution annealed (ksi) | 35 26 | 22.0 21,5 | 145 145 |
Tensile strength alloy 600 - annealed (ksi) alloy 600H - solution annealed (ksi) | 80 73 | 69,5 63,8 | 20.3 20.3 |
Remarks |
Temparature information
Application area | ||
---|---|---|
Operation temperature | 1 ºF to 1652 ºF | |
Explanation report | above 700°C /1292°F alloy 600H is recommended |
Solution heat treatment | ||
---|---|---|
Working temperature | 1976 ºF to 2102 ºF |
Soft annealing | ||
---|---|---|
Working temperature | 1688 ºF to 1832 ºF |
Solution heat treatment | ||
---|---|---|
Working temperature | 2192 ºF to 1652 ºF |
Standards / information
Standards | Desciption |
---|---|
ASTM B 166 | Standard Specification for Nickel-Chromium-Cobald-Molybdenium Alloy rods,bars and wires |
ASTM B 167 | Standard Specification for .... NI-Cr-Fe-alloy seamles pipes and tubes |
ASTM B 168 | Standard Specification for.... Nickel-Chromium-Cobald-Molybdenium Alloy sheet metal and ribbons |
ASTM B 564-06 | Standard Specification for Nickel Alloy Forging |
DIN 17742 (09/2002) | nickel- forgeable alloy with chrome |
DIN 17750 (2002/09) | ribbons and sheet metal out of nickel with nickel-wrought alloy properties |
DIN 17751 (2002/09) | tubes out of nickel with nickel-wrought alloy properties |
DIN 17752 (2002/09) | rod made from nickel with nickel-wrought alloy properties |
DIN 17753 (2002/09) | wire out of nickel with nickel-wrought alloy properties |
DIN EN 10088-1 (09/2005) | Stainless steels Part 1: List of stainless steels |
DIN EN 10095 (05/1999) | heat resistant steel and nickel alloy |
VdTÜV / Werkstoffblatt 305 | nickel chrome iron alloy, NiCr 15 Fe, material-nr. 2.4816 |
Process information
Cold forming | material should be annealed, due to high cold work hardening tendency; metal forming larger than 15% requires intermediate annealing |
---|
Chip removing process | in annealed state |
---|
Welding | |
---|---|
- Material classification acc. CEN ISO/TR 15608 | 43 |
- Type | well weldable WIG plasma welding manual arc welding MIG/MAG submerged arc welding |
- Add. material | 2.4620,2.4806, covered rod electrode 2.4648 |
Main fields of application
Details of application | good resistance to scaling even in high temperatures, good resistance to dry gas ( chloride, hydrogen chloride) up to 1022°F |
---|---|
Certifications | NACE MR 01-75 |
industral furnace engineering | Ofengehäuse-Dichtungen,Transportrollen,Strahlrohre bis Beriebstemperatur von 600°C |
Druckbehälter gem.TRB 100 | -10°C - +450°C |
Chemical Industry | Anlagenteile für Herstellung Chlor und Fluor -Verbindungen Chlor,Chlorwasserstoff ,Flußsäure |
Range of products
Product type | Product |
---|---|
Plates / Sheets | plates/sheets plate/sheet cuts |
Rotating components | fittings from barsteel |
Fittings | welded elbows welded reductions Welded T-pieces seamless elbows seamless reductions seamless T-pieces |
Flanges / Collars / Flared tube ends | flared tube end collars |
Pipes / Tubes | welded pipes/tubes welded square pipes/tubes seamless pipes/tubes |
Bar steel | flat steel section steel round bar steel hexagon steel |
Liability exclusion
All aforementioned specifications serve as a general orientation and have to be reviewed depending on the conditions of use.(c) 2012 M. Woite GmbH, Postbox, D-40671 Erkrath | Phone +49 (211) 24 40 91 - Fax +49 (211) 24 92 28 | www.m-woite.com - woite@woite-edelstahl.com