Material No.: 1.4862
Description
|
|
Chemical Composition
C | S | Si | Mn | Cr | Cu | Ti | Ni | P | Fe | Pb | Sn | ||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|
1.4862 | Min % | 1,50 | 0,80 | 17,00 | 35,00 | balance | |||||||
Max % | 0,10 | 0,03 | 2,50 | 1,50 | 19,00 | 0,50 | 0,20 | 39,00 | 0,03 | balance | |||
(Key to steel 2010) | |||||||||||||
N 08330 | Min % | 0,75 | 17,00 | 34,00 | remainder | ||||||||
Max % | 0,08 | 1,50 | 2,00 | 20,00 | 1,00 | 37,00 | 0,03 | remainder | 0,005 | 0,025 | |||
ASTM B 535 (UNS N 08330) |
Physical properties
Property | Value |
---|---|
Density: lb/in3 | 0,284 |
Hardness: HB (max) | 210 |
Permeabilität bei 20°C | 1,01 |
elasticity modulus (N/mm2) /ksi | 198 /28,7 |
Temperature T °C/F (°C/F) | Specific heat J / kgK (Btu / lb °F) | Thermal conductivity W/mK (Btu·in / ft2·h·°F) | Electric resistance µΩ · cm (Ω circ mill / ft) | Modulus of elasticity kN/mm2 (103 ksi) | Expansion rate from 70°F bis T 10-6 / K (10-6 / °F) |
---|---|---|---|---|---|
20 / 68 | 472 (--) | 11,4 (--) | 103 (--) | 194 (--) | |
100 / 212 | 501 (--) | 12,8 (--) | 106 (--) | 190 (--) | 15,1 (--) |
300 / 572 | 532 (--) | 16,3 (--) | 115 (--) | 177 (--) | 16,2 (--) |
500 /932 | 582 (--) | 19,5 (--) | 120 (--) | 162 (--) | 17,0 (--) |
700 / 1292 | 610 (--) | 22,6 (--) | 123 (--) | 150 (--) | 17,7 (--) |
900 / 1652 | 615 (--) | 25,6 (--) | 127 (--) | 134 (--) | 18,3( --) |
Temp. | Creep strain limit | Creep strain limit | Creep rupture strength | Creep rupture strength | Creep rupture strength |
---|---|---|---|---|---|
°C/°F | 1000h (MPa/ksi) | lösungsgeglüht/ Solution Annealed | |||
750 / 1380 | 49 / 7,1 | ||||
850 / 1560 | 26 / 3,8 | ||||
950 /1740 | 15 / 2,2 | ||||
1050 /1920 | 6,7/ 0,97 |
Temperature | Yield strength in high temperatures | Yield strength in high temperatures | Tensile strenght in high temperatures |
---|---|---|---|
°C/°F | Rp 0,2 | Rp 1,0 | Rm | min. (N/mm2/ksi) | min. (N/mm2/ksi) | N/mm2 /ksi |
20 / 68 | 285 40,6 | 310 / 44,9 | 650 / 94,2 |
100 / 212 | 265 / 30,4 | 290 / 34,8 | 630 / 91,4 |
200 / 392 | 240 / 26,1 | 265 / 30,4 | 615 / 84,1 |
300 / 572 | 220 / 23,9 | 250 / 28,3 | 605 / 76,9 |
400 / 752 | 210 / 21,7 | 235 / 26,1 | 555/ 72,5 |
500 / 932 | 200 / 19,5 | 225 / 23,9 | 470 / 68,1 |
700 / 1292 | 175 / 25,3 | 190 / 27,5 | 340 / 49,3 |
900 /1652 | 85 / 12,3 | 100 / 14,5 | 120 / 17,4 |
ksi value calculated |
Mechanical properties (20°C / 68°F)
Yield strength Mpa/ ksi | <=280 /<=40,6 | ||
---|---|---|---|
Yield strength Mpa/ ksi | <=310/<=44,9 | ||
Tensile strenght Rm N/mm2 | <=650/<=94,2 |
Temparature information
Solution heat treatment | ||
---|---|---|
Working temperature | 2102 ºF to 1742 ºF |
Solution heat treatment | ||
---|---|---|
Working temperature | 2192 ºF to 1652 ºF |
soft annealing |
---|
Standards / information
Standards | Desciption |
---|
Process information
Chip removing process | process in annealed state due to cold work hardening low cutting speed keep constant cutting tool contact |
---|
Welding | |
---|---|
- Type | well weldable WIG manual arc welding MiG |
Main fields of application
Details of application | |
---|---|
Certifications | |
industral furnace engineering |
Range of products
Product type | Product |
---|---|
Plates / Sheets | plates/sheets |
Fittings | welded elbows welded reductions Welded T-pieces seamless elbows seamless reductions seamless T-pieces Other Fittings a.o. Weldolets, Nipples |
Flanges / Collars / Flared tube ends | various flanges (weld neck flange,blind flange etc.) |
Bumped boiler ends / caps / round blanks | from sheets |
Pipes / Tubes | welded pipes/tubes seamless pipes/tubes |
Bar steel | flat steel round bar steel |
Liability exclusion
All aforementioned specifications serve as a general orientation and have to be reviewed depending on the conditions of use.(c) 2012 M. Woite GmbH, Postbox, D-40671 Erkrath | Phone +49 (211) 24 40 91 - Fax +49 (211) 24 92 28 | www.m-woite.com - woite@woite-edelstahl.com