Material No.: 1.4307
Description
|
|
Chemical Composition
| C | Si | Mn | P | Cr | N | Ni | S | ||
|---|---|---|---|---|---|---|---|---|---|
| 1.4307 | Min % | 17,50 | 8,00 | ||||||
| Max % | 0,03 | 1,00 | 2,00 | 0,045 | 19,50 | 0,110 | 10,50 | ||
| (Key to steel 2010) | |||||||||
| AISI 304L S 30403 | Min % | 18,00 | 10,00 | ||||||
| Max % | 0,035 | 0,75 | 2,oo | 0,040 | 20,00 | 13,00 | 0,030 | ||
| ASTM A 213 S 30403 | |||||||||
Physical properties
| Property | Value |
|---|---|
| Density: kg/dm3 | 7,9 |
| Hardness: HB | 195 |
| Rockwell Hardness Number max. | B90 (TP304 -ASTM A 249) |
| magnetizable | non |
| polishable | yes |
| Temperature T °C/F (°C/F) | Specific heat J / kgK (Btu / lb °F) | Thermal conductivity W/mK (Btu·in / ft2·h·°F) | Electric resistance µΩ · cm (Ω circ mill / ft) | Modulus of elasticity kN/mm2 (103 ksi) | Expansion rate from 70°F bis T 10-6 / K (10-6 / °F) |
|---|---|---|---|---|---|
| 20 / 68 | 500 | 15 |
| Temperature | E-Modul | 0.2% Yield strength in high temperatures | 1,0% Yield strength in high temperatures |
|---|---|---|---|
| °C/°F | Rp0,2 | Rp1,0 | Mpa | Mpa/ksi | Mpa/ksi |
| 20°/68° | 200000 | >180/>26,1 | >215/>31,2 |
| 100°/212° | 194000 | >147/>21,3 | >181/>26,25 |
| 300°/572° | 179000 | >100/14,5 | >127/>18,4 |
| 500°/932° | 165000 | >81/11,74 | >109/>15,8 |
Mechanical properties (20°C / 68°F)
| Yield strenght ksi /(Mpa) | 25 (170) | TP 304L ASTM A 249 | |
|---|---|---|---|
| tensile strenght (Mpa)ksi | 450-680 | ||
| Elongation(A5) (%) | 51 | ||
| otched impact strength ISO-VI(J) | 225 | ||
Temparature information
| Application area | ||
|---|---|---|
| Operation temperature | ºF to 1112 ºF | ???? |
| Solution heat treatment | ||
|---|---|---|
| Working temperature | 1832 ºF to 2012 ºF | |
| Explanation report | cool down:air,Water | |
| Solution heat treatment | ||
|---|---|---|
| Working temperature | 1382 ºF to 2102 ºF | |
| Explanation report | cool down: air | |
Standards / information
| Standards | Desciption |
|---|---|
| ASTM A 249 | Standard Specification for Welded austenitic steel boiler, Superheaters, heat-exchangers,and condenser Tubes |
| ASTM A 269 | Standard Specification for Seamless and welded, austenic, and stainless steel tubing for general purposes |
| ASTM A 479 | Rods and cross-sections made of stainless and heat-resistant steel used in boilers and other pressure tanks |
| DIN 10216-5 (11/2004+B1) | Seamless steel pipes under compression load Pipes made from stainless steel |
| DIN EN 10088-1 (09/2005) | Stainless steels Part 1: List of stainless steels |
| DIN EN 10088-3 (09/2005) | stainless steels.Technical delivery conditions for semi-finished products,bars,rods,wire selection and bright products of corrosion resisting steels for general and construction purposes |
| DIN EN 10296-2 (02/2006) | Welded circular steel pipes for machine construction and general technical service stainless steel |
Process information
| Welding | |
|---|---|
| - Type | gas fusion welding manual arc protective gas resistance welding |
| - Add. material | 1.4316 |
| - Hints | no heat treatment necessary before or after welding process |
Main fields of application
| Details of application | |
|---|---|
| Certifications | |
| Chemical Industry | |
| crude oil | |
| petrochemical industry | |
| food processing industry | |
| building industry |
Range of products
| Product type | Product |
|---|---|
| Plates / Sheets | plates/sheets plate/sheet cuts |
| Fittings | welded elbows welded reductions Welded T-pieces seamless elbows seamless reductions seamless T-pieces |
| Pipes / Tubes | welded pipes/tubes seamless pipes/tubes |
| Round bar | peeled |
| Bar steel | flat steel round bar steel |
Liability exclusion
All aforementioned specifications serve as a general orientation and have to be reviewed depending on the conditions of use.(c) 2012 M. Woite GmbH, Postbox, D-40671 Erkrath | Phone +49 (211) 24 40 91 - Fax +49 (211) 24 92 28 | www.m-woite.com - woite@woite-edelstahl.com