high corrosion resistance
DIN | Alloy | UNS | AISI | AFNOR | B.S. | Registered work's label |
---|---|---|---|---|---|---|
1.4306 | S 30403 | AISI 304L | Z3CN19-11 | 304S11 | ||
1.4465 | S 31050 | Cronifer 2525 LCN | ||||
1.4547 | S 31254 | X1CrNiMoCuN20-18-7 / NF EN 10217-7 (02/2005) (FR) | X1CrNiMoCuN20-18-7 / B.S.EN 10217-7 (02/2005) (GB) | 254 SMO® | ||
1.4562 | Alloy 31 | N 08031 | Nocrofer® 3127 hMo | |||
1.4571 | S 31635 | AISI 316 Ti | X6CrNiMoTi 17-12-2 / NF EN 10088-1 ( 06/2005) (FR) | X6CrNiMoTi 17-12-2 /B.S. EN 10088-1 ( 06/2005) (GB) | Cronifer 1810Ti | |
1.4878 | S 32109 | X8CrNiTi18 10 /NF EN 10088-1 (06/2005) (FR) | X8CrNiTi18 10 /NF EN 10088-1 (06/2005) (GB) | |||
2.4602 | alloy 22 | N 06022 | Hastelloy® C22 | |||
2.4610 | alloy C-4 | N 06455 | Hastelloy®C4 Nicrofer® 6616 hMo |
- usable in oxidising substances, if forming a passivating oxide coating
- performs especially well under reducing conditions
- resistant to intercrystalline corrosion
- resistance to intercristalline corrosion up to 0.2"
- durch Titanzusatz Verbesserung der interkristallinen Korrosion,aber Verschlechterung der Zerspanbarkeit
- against crevice corrosion
- good resistance to intercrystalline corrosion
- good against chloride induced tensile corrosion
- good resistance to chloride induced tensile corrosion
- good resistance to tensile corrosion
- Good overall corrosion resistance
- good resistance to intercristalline corrosion to ca. 572° F (ca 300°C)
- good resistance even in carbonising/chlorinating/oxidising substances
- high resistance to corrosion in oxidising and chloric substances
- high resistance to pitting corrosion, tensile corrosion, crevice corrosion
- high resistance to pitting corrosion in oxidising and reducing substances
- non-corroding
- stainless
- satisfactionary against pitting corrosion
- +++#1:bis ca. 400°C
- +++#1:durch Molybdänzusatz
- +++#1:(nicht im geschweißtem Zustand)
- +++#1:< 400°C
- +++#2: bis 5mm
- +++#:<350°C
- +++<= 50mm
Liability exclusion
All aforementioned specifications serve as a general orientation and have to be reviewed depending on the conditions of use.(c) 2012 M. Woite GmbH, Postbox, D-40671 Erkrath | Phone +49 (211) 24 40 91 - Fax +49 (211) 24 92 28 | www.m-woite.com - woite@woite-edelstahl.com