no heat treatment necessary before or after welding process
| DIN | Alloy | UNS | AISI | AFNOR | B.S. | Registered work's label |
|---|---|---|---|---|---|---|
| 1.4306 | S 30403 | AISI 304L | Z3CN19-11 | 304S11 | ||
| 1.4307 | S 30403 | AISI 304L | Z3CN19-09 | 304S11 | ||
| 1.4841 | S 31000 S 31400 | AISI 310 AISI 314 | X15CrNiSi 25-21 / EN 10088-1( 06/2005) (FR) | X15CrNiSi 25-21 / EN 10088-1( 06/2005) (GB) | Cronifer® 2520 | |
| 1.4845 | S 31008 S 31009 | AISI 310 S | Z 12 CN 25-20 | 310 S 24 | ||
| 2.4605 | alloy 59 | N 06059 | Nicrofer®5923 hMo Hastelloy®59alloy Inconel®alloy 59 |
- pre-heat to 392°F if material width >0.4"
- when using covered rod electrodes, mind the low C and Si content
- Beim Schweißen unter Gas kein wasserstoff-oder stickstoffhaltiges Gas verwenden
- ???
- preheating not required
- avoid gas welding
- gezielte Wärmeführung
- generally no heat treatment necessary after welding process
- special post heat treating not required
- use material in soft-annealed state
- Material im weichgeglühtem Zustand vorliegen
- material is heat-sensitive , requires low heat input
- material has to be normalized or tempered
- normal weldability
- Vorwärm- und Arbeitstemperatur max.200°C
- pre-heat 302°F
- pre-heat 212°F (>10mm)
- pre-heat 662°F
- material is weldable in all widths using aforementioned techniques
- interpass temperature must not go over 302°F
- Zwischenlagetemperatur max 120°C
Liability exclusion
All aforementioned specifications serve as a general orientation and have to be reviewed depending on the conditions of use.(c) 2012 M. Woite GmbH, Postbox, D-40671 Erkrath | Phone +49 (211) 24 40 91 - Fax +49 (211) 24 92 28 | www.m-woite.com - woite@woite-edelstahl.com