Material No.: AISI 405
Description
|
|
Chemical Composition
C | Si | Mn | P | S | AL | Cr | Ni | N | ||
---|---|---|---|---|---|---|---|---|---|---|
AISI 405 | Min % | |||||||||
Max % | ||||||||||
1.4724 | Min % | 0,70 | 0,70 | 12,00 | ||||||
Max % | 0,12 | 1,40 | 1,00 | 0,040 | 0,015 | 1,20 | 14,00 | |||
(Key to steel 2010) | ||||||||||
S 44600 | Min % | 23,00 | ||||||||
Max % | 0,20 | 1,00 | 1,50 | 0,040 | 0,030 | 27,00 | 0,75 | 0,25 | ||
ASTM A268 (UNS S44600) |
Physical properties
Property | Value |
---|---|
Density: kg/dm3 | 7,7 |
Hardness: HB | <=192 |
magnetizable | yes |
Temperature T °C/F (°C/F) | Specific heat J / kgK (Btu / lb °F) | Thermal conductivity W/mK (Btu·in / ft2·h·°F) | Electric resistance µΩ · cm (Ω circ mill / ft) | Modulus of elasticity kN/mm2 (103 ksi) | Expansion rate from 70°F bis T 10-6 / K (10-6 / °F) |
---|---|---|---|---|---|
20 / 68 | 500 (--) | 21 (--) | 200 (--) |
Temp. | Creep strain limit | Creep strain limit | Creep rupture strength | Creep rupture strength | Creep rupture strength |
---|---|---|---|---|---|
°C / °F | 1000 h | 10 000h | Rp 1,0 (MPa) (geglüht) | Rp 1,0 (MPa) (geglüht) | |
600 /1112 | 27,5 | 35 | |||
800 /1472 | 3,7 | 4,3 | |||
900 / 1652 | 1,8 | 1,9 | |||
1000 / 1832 | 0,5 |
Mechanical properties (20°C / 68°F)
0,2%Yield strength Rp0,2N7mm2/ksi | 250 / 36,2 | ||
---|---|---|---|
Tensile strenght Rm N/mm2/ksi | 450-650/65,2-94,2 | ||
Elongation A5 (%) | <=15 |
Temparature information
Application area | ||
---|---|---|
Operation temperature | ºF to 1562 ºF | by air to ca 1472°F (resistant to scaling) |
soft annealing | ||
---|---|---|
Working temperature | 1472 ºF to 1580 ºF |
Solution heat treatment | ||
---|---|---|
Working temperature | 2012 ºF to 1472 ºF |
annealing | ||
---|---|---|
Working temperature | 1472 ºF to 1562 ºF | afterwards: Ferrit |
Standards / information
Standards | Desciption |
---|---|
ASTM A 276 | Rods and cross-sections made of stainless and heat-resistant steel |
Process information
Chip removing process | good machinability |
---|
Welding | |
---|---|
- Add. material | 1.4502,1.4723,1.4773,1.4820 |
Main fields of application
Details of application | performs well under sulfidising conditions |
---|---|
Certifications | |
petrochemical industry | |
industral furnace engineering | |
Steam boiler construction |
Range of products
Product type | Product |
---|---|
Processing / Construction | from sheets |
Plates / Sheets | plates/sheets plate/sheet cuts |
Fittings | welded elbows welded reductions Welded T-pieces seamless elbows seamless reductions seamless T-pieces |
Flanges / Collars / Flared tube ends | various flanges (weld neck flange,blind flange etc.) |
Pipes / Tubes | welded pipes/tubes seamless pipes/tubes |
Round bar | peeled |
Bar steel | section steel round bar steel |
Liability exclusion
All aforementioned specifications serve as a general orientation and have to be reviewed depending on the conditions of use.(c) 2012 M. Woite GmbH, Postbox, D-40671 Erkrath | Phone +49 (211) 24 40 91 - Fax +49 (211) 24 92 28 | www.m-woite.com - woite@woite-edelstahl.com