Material No.: 2.4619
Description
|
| ||||||||||||||||||||
|
Chemical Composition
C | Mn | P | S | Cr | Mo | Si | Co | Fe | Ni | Cu | Nb+Ta | W | Cb(Nb) | ||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
2.4619 | Min % | 21,00 | 6,00 | 18,00 | balance | 1,50 | |||||||||
Max % | 0,015 | 1,00 | 0,025 | 0,015 | 23,50 | 8,00 | 1,00 | 5,00 | 21,00 | balance | 2,50 | 0,50 | 1,50 | ||
(Key to Steel 2010) | |||||||||||||||
alloy G3 N 06985 | Min % | 21,00 | 6,00 | 18,00 | balance | 1,50 | |||||||||
Max % | 0,015 | 1,00 | 0,04 | 0,03 | 23,50 | 8,00 | 1,00 | 5,00 | 21,00 | balance | 2,50 | 1,50 | 0,50 | ||
ASTM B 622 |
Physical properties
Property | Value |
---|---|
Density: ln/in.3 | 0,30 |
Hardness: HB | 240 |
Permeability at 20°C/68°F | < 1,01 |
Temperature T °C/F (°C/F) | Specific heat J / kgK (Btu / lb °F) | Thermal conductivity W/mK (Btu·in / ft2·h·°F) | Electric resistance µΩ · cm (Ω circ mill / ft) | Modulus of elasticity kN/mm2 (103 ksi) | Expansion rate from 70°F bis T 10-6 / K (10-6 / °F) |
---|---|---|---|---|---|
20 / 68 | 441 / 0,105 | 11.1 / 77 | 115 | 211 | |
100 / 212 | 452 | 12.6 /... | 117 | 205 | 14,3 |
204 /400 | ..../0,110 | ..../ 99 | 119 | 199 | 14,7 |
300 / 572 | 471/ .... | 16.0 /... | 121 | 192 | 15,0 |
427 / 800 | .... /0,115 | ..../ 126 | 123 | 186 | 15,3 |
538 /100 | .... /0,117 | .../ 137 | 125 | 180 | 15,7 |
600 /1112 | 495 | 21.0 /... | 126 | 173 | 16,1 |
649 /1200 | ..../ 0,119 | ..../ 151 | 127 | 167 | 16,5 |
700 /1292 | 503 /... | 22,6 /... |
Mechanical properties (20°C / 68°F)
Yield strength (0,2% offset) ksi | 35-30 | ||
---|---|---|---|
Yield strength(1% offset) ksi | 33-38 | ||
Tensile strength min.ksi | 90-85 | ||
Elongation A5 % | 35-45 | ||
Remarks |
Temparature information
Solution heat treatment | ||
---|---|---|
Working temperature | 2012 ºF to 2120 ºF | |
Explanation report | quick cooling with air/water |
Solution heat treatment | ||
---|---|---|
Working temperature | 2246 ºF to 1742 ºF | |
Explanation report | cooling with air |
Standards / information
Standards | Desciption |
---|---|
ASTM B 619 | Standard Spezifikation for Welded Nickel and Alloy Pipe |
ASTM B 622 | Standard Specification for Seamless Nickel and Nickel-Cobalt Alloy Pipe and Tube |
ASTM B 626 | Standard Specification for Welded Nickel and Nickel-Cobalt Alloy Tube |
DIN 17744 (2002/09) | nickel-forgeable alloy with molybdenum and chrome |
DIN 17750 (2002/09) | ribbons and sheet metal out of nickel with nickel-wrought alloy properties |
DIN 17751 (2002/09) | tubes out of nickel with nickel-wrought alloy properties |
DIN 17752 (2002/09) | rod made from nickel with nickel-wrought alloy properties |
Process information
Welding | |
---|---|
- Type | well weldable |
- Add. material | covered rod electrode 2.4621 |
Main fields of application
Details of application | Alloy 2.4619 (alloy G-3) is used in flue gas scrubbers, and with phosphoric and sulphuric acid. |
---|---|
Certifications | NACE Mr 01-75 |
offshore plants | |
sea and lake water plants | |
petrochemical industry | Petrochemische Anlagen |
Chemical Industry | Essigsäureanlagen |
Fertiliser industry | |
drilling equipment | acid gas production |
Range of products
Product type | Product |
---|---|
Bar steel | hexagon steel |
Liability exclusion
All aforementioned specifications serve as a general orientation and have to be reviewed depending on the conditions of use.(c) 2012 M. Woite GmbH, Postbox, D-40671 Erkrath | Phone +49 (211) 24 40 91 - Fax +49 (211) 24 92 28 | www.m-woite.com - woite@woite-edelstahl.com