Material No.: 1.4713
Description
|
|
Chemical Composition
C | Si | Mn | Cr | Al | P | S | ||
---|---|---|---|---|---|---|---|---|
1.4713 | Min % | 0,50 | 6,00 | 0,50 | ||||
Max % | 0,12 | 1,00 | 1,00 | 8,00 | 1,00 | 0,04 | 0,015 | |
(Key to steel 2010) |
Physical properties
Property | Value |
---|---|
Density: kg/dm3 | 7,7 |
Hardness: HB30 | <=192 |
magnetizable | yes |
Temperature T °C/F (°C/F) | Specific heat J / kgK (Btu / lb °F) | Thermal conductivity W/mK (Btu·in / ft2·h·°F) | Electric resistance µΩ · cm (Ω circ mill / ft) | Modulus of elasticity kN/mm2 (103 ksi) | Expansion rate from 70°F bis T 10-6 / K (10-6 / °F) |
---|---|---|---|---|---|
20/ 68 | 0,424 (--) | 20,5 (--) | 215 (--) | ||
500/ 932 | 25 (--) |
Temp. | Creep strain limit | Creep strain limit | Creep rupture strength | Creep rupture strength | Creep rupture strength |
---|---|---|---|---|---|
( °C / °F) | 1000 h (Rp1,0) | 10 000h | (°C/°F) | Mpa 7 ksi | Mpa / ksi |
600 /1112 | 27,5 / 4,0 | 35 / 5,0 | |||
700 / 1292 | 8,5 /1,2 | 9,5 / 1,3 | |||
900 / 1652 | 1,8 / 0,3 | 1,9 / 0,3 | |||
1000 / 1832 | 0,5 /<1,0 | ||||
ksi value calculated |
Mechanical properties (20°C / 68°F)
Yield strength Rp0,2 (N/mm2) | >=220 | (0,5-7mm) | |
---|---|---|---|
tensile strength Rm (N/mm2) | 420-620 | (0,5-7mm) | |
elongation A5 (%) | >=20% lengthwise >=15% transverse | (3-7mm) (3-7mm) |
Temparature information
Application area | ||
---|---|---|
Operation temperature | ºF to 1472 ºF | by air to ca 1472°F (resistant to scaling) |
soft annealing | ||
---|---|---|
Working temperature | 1436 ºF to 1544 ºF | |
Explanation report | cool down .air,water |
Solution heat treatment | ||
---|---|---|
Working temperature | 2012 ºF to 1382 ºF | |
Explanation report | coll down:air |
annealing | ||
---|---|---|
Working temperature | 1382 ºF to 1472 ºF | afterwards: Ferrit, Perlit |
Standards / information
Standards | Desciption |
---|---|
DIN EN 10088-1 (09/2005) | Stainless steels Part 1: List of stainless steels |
DIN EN 10095 (05/1999) | heat resistant steel and nickel alloy |
SEW 310 (08/1992) | physical properties of steel |
SEW 470 (02/1976) | heat-resisting rolled and forged steels |
Process information
Chip removing process | good machinability |
---|
Welding | |
---|---|
- Type | manual arc submerged arc welding WIG |
- Add. material | 1.4370,1.4551,1.4716,1.4723,1.4820,1,4829 |
Main fields of application
Details of application | |
---|---|
Certifications | |
Power engineering | |
Power plants | header |
industral furnace engineering | steel pipes furnace parts transport rollers |
Range of products
Product type | Product |
---|---|
Plates / Sheets | plates/sheets plate/sheet cuts |
Fittings | welded elbows welded reductions Welded T-pieces seamless elbows seamless reductions seamless T-pieces |
Flanges / Collars / Flared tube ends | various flanges (weld neck flange,blind flange etc.) |
Pipes / Tubes | welded pipes/tubes |
Bar steel | flat steel round bar steel |